Method For Manufacturing Pneumatic Tire

ABSTRACT

A method for manufacturing a pneumatic tire may include lap-splicing end parts of a laminate sheet in which a sheet obtained from a thermoplastic resin or a thermoplastic resin composition of a thermoplastic resin blended with an elastomer is laminated with a rubber that undergoes vulcanizing adhesion with the thermoplastic resin or the thermoplastic resin composition. After the sheet obtained from the thermoplastic resin or the thermoplastic resin composition is cut into lengths to be supplied for lap-splicing, and at a stage before tire vulcanization molding, distal end parts of the sheet obtained from the thermoplastic resin or the thermoplastic resin composition are sharpened with a thermal treatment.

TECHNICAL FIELD

The present invention relates to a method for manufacturing a pneumatictire.

More specifically, the present invention relates to a method formanufacturing a pneumatic tire by cutting, into certain lengths, alaminate sheet in which a sheet obtained from a thermoplastic resin or athermoplastic resin composition of a thermoplastic resin blended with anelastomer is laminated with a rubber that undergoes vulcanizing adhesionto the thermoplastic resin or the thermoplastic resin composition;splicing the end parts of the laminate sheet; and then performingvulcanization molding; wherein, the pneumatic tire durably demonstratesthe characteristics and performance of the laminate sheet over anextended period of time without the generation of cracks in the vicinityof the splice portion of the spliced laminate sheet after a pneumatictire manufactured with this method begins traveling.

The laminate sheet typically constitutes an inner liner layer that is,for example, one of the important members in recent pneumatic tires. Inthis case, the present invention relates to a pneumatic tire having aninner liner layer formed with the laminate sheet as described above, andto a method for manufacturing the pneumatic tire with the inner linerlayer having superior durability without the generation of cracks in thevicinity of a splice portion of the spliced laminate sheet (inner linerlayer) after traveling with the pneumatic tire has begun.

Other than the inner liner layer, the laminate sheet may be used, forexample, in an important location in the tire as a member for reducingthe weight and improving the strength of the tire without theaccompaniment of an excessive increase in mass. In this case, thepresent invention relates to a method for manufacturing a pneumatic tirethat uses a reinforcing sheet formed from the laminate sheet asdescribed above, and to a method for manufacturing a pneumatic tire withthe reinforcing sheet having the effect of superior durability withoutthe generation of cracks in the vicinity of a splice portion of thespliced reinforcing sheet.

BACKGROUND

Recently, the use of a sheet-like pneumatic tire inner liner obtainedfrom a thermoplastic resin or a thermoplastic resin composition of athermoplastic resin blended with an elastomer, has been proposed andstudied (Patent Document 1).

When actually using a sheet-like object obtained from the thermoplasticresin or the thermoplastic resin composition of a thermoplastic resinblended with an elastomer in a pneumatic tire inner liner, normally amanufacturing technique of winding a laminate sheet of the sheetobtained from the thermoplastic resin or the thermoplastic resincomposition of a thermoplastic resin blended with an elastomer and arubber (tie rubber) sheet that undergoes vulcanizing adhesion to thesheet-like object obtained from the thermoplastic resin or thethermoplastic resin composition of a thermoplastic resin blended with anelastomer, onto a tire molding drum, performing a lap splic, and thensupplying to the tire vulcanization molding process is performed.

However, when a tire is manufactured by winding the abovementionedlaminate sheet into a laminate sheet, pulling and cutting the laminatesheet into portions of a required length, then winding the cut lengthsonto the tire molding drum for lap splicing and then performingvulcanization molding, separation may occur between the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition thatconstitutes the inner liner, and the tie rubber sheet for vulcanizingadhesion with the sheet obtained from the thermoplastic resin or thethermoplastic resin composition, after the tire has started traveling.

When explained with reference to a drawing as illustrated in FIG. 2A, alaminate sheet 1, in which a sheet 2 obtained from a thermoplastic resinor a thermoplastic resin composition of a thermoplastic resin blendedwith an elastomer is laminated with a tie rubber layer 3, is cut intocertain sizes (lengths) with a blade or the like and then lap-spliced ona tire molding drum so that a ring-like lap splice portion S is formedat both end parts of the laminate sheet 1. When one laminate sheet 1 isused, both end parts are lap-spliced so that a ring shape is formed, andwhen a plurality of the laminate sheets 1 are used, the mutual end partsof each of the laminate sheets 1 are lap-spliced together so that onering shape is formed with the plurality of sheets.

Next, other parts (not shown) required for tire manufacturing are woundand the tire undergoes vulcanization molding with a bladder.

After the vulcanization molding, an inner liner layer 10 is formedincluding the tie rubber layer 3 and the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer, and an exposed portionand a portion embedded in the tie rubber layer of the sheet 2 obtainedfrom the thermoplastic resin or the thermoplastic resin composition areformed in the vicinity of a lap splice part S as illustrated in FIG. 2B.

The phenomenon of the sheet 2 obtained from the thermoplastic resin orthe thermoplastic resin composition and the vulcanizing-adhered tierubber sheet 3 separating is produced where the sheet 2 obtained fromthe thermoplastic resin or the thermoplastic resin composition isexposed and at a distal end part vicinity 4, and the phenomenon firstinvolves a crack being produced and the crack growing so that thephenomenon of the separation of the sheet 2 continues to grow.

While the above explanation describes the use of the laminate sheet 1obtained from the tie rubber layer 3 and the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition, as the innerliner layer, the same can be said when the laminate sheet 1 is used as amember other than the inner liner layer such as, for example, areinforcing sheet layer (not shown) disposed over the entirecircumferential direction on the tire external periphery side of theinner liner layer. In particular, tire locations in which the laminatesheet is disposed as the reinforcing sheet layer are normally used undersevere conditions such as when a load is applied repetitively over along period of time and these locations often suffer from the problemsof the occurrence of cracks and/or separation.

PRIOR ART DOCUMENTS Patent Documents

Patent Document 1: Japanese Unexamined Patent Application PublicationNo. 2009-241855

SUMMARY OF THE INVENTION Problems to be Solved by the Invention

In view of the points discussed above, an object of the presentinvention is to provide a method for manufacturing a pneumatic tirehaving an inner liner layer or a reinforcing sheet layer formed by lapsplicing (providing an overlap portion when performing a splice) endparts of a laminate sheet in which a sheet obtained from a thermoplasticresin or a thermoplastic resin composition of a thermoplastic resinblended with an elastomer is laminated with a rubber that undergoesvulcanizing adhesion with the thermoplastic resin or the thermoplasticresin composition, then performing vulcanization molding to form thelaminate sheet, wherein, the pneumatic tire favorably demonstrates, withgood durability, characteristics and performance of the laminate sheetover an extended period of time without the generation of cracks and/orseparation near the spliced portions of the spliced laminate sheet (theinner liner layer or the reinforcing sheet layer) after a pneumatic tiremanufactured with this method begins traveling.

Means to Solve the Problem

The method for manufacturing the pneumatic tire of the present inventionthat satisfies the above object has the following constitution (1).

(1) A method for manufacturing a pneumatic tire having a step oflap-splicing end parts of a laminate sheet in which a sheet obtainedfrom a thermoplastic resin or a thermoplastic resin composition of athermoplastic resin blended with an elastomer, is laminated with arubber that undergoes vulcanizing adhesion with the thermoplastic resinor the thermoplastic resin composition, wherein, after the sheetobtained from the thermoplastic resin or the thermoplastic resincomposition is cut into lengths to be supplied to the lap-splicing step,and at a stage before a tire vulcanization molding step, distal endparts of the sheet obtained from the thermoplastic resin or thethermoplastic resin composition are sharpened with a thermal treatment.

The method for manufacturing the pneumatic tire of the above presentinvention desirably includes any of the following constitutions (2) to(8).

(2) The method for manufacturing the pneumatic tire described in (1),wherein a temperature of the thermal treatment is at or above themelting point of the thermoplastic resin or the thermoplastic resincomposition.

(3) The method for manufacturing the pneumatic tire described in (2),wherein, when the thermal treatment is conducted solely on the sheetobtained from the thermoplastic resin or the thermoplastic resincomposition, the thermal treatment is conducted at a temperature at orabove the melting point of the thermoplastic resin or the thermoplasticresin composition and at or below (the melting point of thethermoplastic resin or the thermoplastic resin composition +250° C.).

(4) The method for manufacturing the pneumatic tire described in (2),wherein, when the thermal treatment is conducted on the laminate sheetin which the sheet obtained from the thermoplastic resin or thethermoplastic resin composition is laminated with a rubber thatundergoes vulcanizing adhesion with the thermoplastic resin or thethermoplastic resin composition, the thermal treatment is conducted at atemperature at or above the melting point of the thermoplastic resin orthe thermoplastic resin composition and at or below (the melting pointof the thermoplastic resin composition +180° C.).

(5) The method for manufacturing the pneumatic tire described in any of(1) to (4), wherein, the sharpening has a relationship in which athickness T (mm) at a position at a distance inward by a length of (t×⅓)from the distal end of the sheet obtained from the thermoplastic resinor the thermoplastic resin composition, satisfies 0.1t≦T≦0.8t.

where,

t: average thickness (mm) in the tire circumferential direction of aportion not subject to the sharpening of the sheet obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer.

T: thickness (mm) at a position at a distance inward by a length of(t×⅓) from the distal end of the sheet obtained from the thermoplasticresin or the thermoplastic resin composition of a thermoplastic resinblended with an elastomer.

(6) The method for manufacturing the pneumatic tire described in any of(1) to (5), wherein, the thermoplastic resin includes at least one typeof a polyamide resin, a polyester resin, a polynitrile resin, apolymethacrylate resin, a polyvinyl resin, a cellulose resin, a fluorideresin, and an imide resin.

(7) The method for manufacturing the pneumatic tire described in any of(1) to (6), wherein, the elastomer includes at least one type of adiene-based rubber, a diene-based rubber hydrogenate, ahalogen-containing rubber, a silicon rubber, a sulfur-containing rubber,a fluororubber, and a thermoplastic elastomer.

(8) The method for manufacturing the pneumatic tire described in any of(1) to (7), wherein, one or a plurality of the laminate sheets are used,and both end parts are lap-spliced when one sheet is used, and mutualend parts are lap-spliced when a plurality of sheets are used.

EFFECTS OF THE INVENTION

According to the present invention described in claim 1, a method formanufacturing a pneumatic tire is provided, wherein an inner liner layeror a reinforcing sheet layer formed by lap splicing end parts of alaminate sheet in which a sheet obtained from a thermoplastic resin or athermoplastic resin composition of a thermoplastic resin blended with anelastomer is laminated with rubber that undergoes vulcanizing adhesionwith the thermoplastic resin or the thermoplastic resin composition,then performing vulcanization molding to form the laminate sheet,wherein, the pneumatic tire favorably demonstrates, with gooddurability, characteristics and performance of the laminate sheet overan extended period of time without the generation of cracks and/orseparation in the vicinity of the spliced portions of the splicedlaminate sheet (the inner liner layer or the reinforcing sheet layer)after a pneumatic tire manufactured with this method begins traveling.

According to the present invention as in claim 2, a method formanufacturing a pneumatic tire is provided, wherein the method has theeffect of the method of the present invention described in claim 1 andis able to clearly demonstrate the effect.

According to the present invention as in any of claims 3 to 5, a methodfor manufacturing a pneumatic tire is provided, wherein the method hasthe effect of the method of the present invention described in claim 1and is able to clearly demonstrate the effect.

According to the present invention as in claim 6, a method formanufacturing a pneumatic tire is provided, wherein the method has theeffect of the method as in claim 1, and enables the fabrication of alaminate sheet obtained from the thermoplastic resin or thethermoplastic resin composition that, upon the appropriate selection ofthe thermoplastic resin, satisfies the expected properties of gaspermeability, durability, flexibility, heat resistance, orprocessability, when the laminate sheet is used as a member.

According to the present invention as in claim 7, a method formanufacturing a pneumatic tire is provided, wherein the method has theeffect of the method as in claim 1, and enables the fabrication of alaminate sheet obtained from the thermoplastic resin or thethermoplastic resin composition that, upon the appropriate selection ofan elastomer, satisfies the expected properties of durability,flexibility, or processability, when the laminate sheet is used as amember.

According to the present invention as in claim 8, a method formanufacturing a pneumatic tire is provided, wherein the method has theeffect of the method as in claim 1, and enables the manufacture of anysize of pneumatic tire by appropriately changing an overlap amount(overlapping portion length in tire circumferential direction) of a lapsplice part of the laminate sheet and/or appropriately changing thenumber of laminate sheets used according to the tire size.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a method of the present invention wherein, (a) is amodel for illustrating the laminate sheet 1 in which the sheet 2obtained from the thermoplastic resin or the resin composition islaminated with the rubber 3 that undergoes vulcanizing adhesion with thethermoplastic resin or the resin composition, is cut into certainlengths and sharpened at the distal ends thereof, both distal ends ofthe laminate sheet 1 being lap-spliced together; (b) is a model forillustrating the state illustrated in (a) after the vulcanizationmolding; and (c) is an approximate side view for illustrating the sheet2 (single state) obtained from the thermoplastic resin or thethermoplastic resin composition in which the distal ends thereof aresubject to the sharpening.

FIG. 2 illustrates a method other than the present invention wherein,(a) is a model for illustrating the laminate sheet 1 in which the sheet2 obtained from the thermoplastic resin or the resin composition islaminated with the rubber 3 that undergoes vulcanizing adhesion with thethermoplastic resin or the resin composition, is cut into certainlengths and subject to the sharpening at the distal ends thereof, bothdistal ends of the laminate sheet 1 being lap-spliced together; (b) is amodel for illustrating the state illustrated in (a) after thevulcanization molding; and (c) is an approximate side view forillustrating the sheet 2 (single state) obtained from the thermoplasticresin or the thermoplastic resin composition in which the distal endsthereof are subject to the sharpening.

FIG. 3 is a partial fragmented perspective view illustrating one exampleof an aspect of the pneumatic tire according to the method formanufacturing a pneumatic tire of the present invention.

DESCRIPTION OF EMBODIMENTS

The following is a detailed description of a method for manufacturing apneumatic tire of the present invention.

A method for manufacturing a pneumatic tire has a step of lap splicingend parts of a laminate sheet 1 in which a sheet 2 obtained from athermoplastic resin or a thermoplastic resin composition of athermoplastic resin blended with an elastomer is laminated with a rubber3 that undergoes vulcanizing adhesion with the thermoplastic resin orthe thermoplastic resin composition, wherein, after the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition iscut into lengths to be supplied to the lap-splicing step, and at a stagebefore a tire vulcanization molding step, distal end parts of the sheet2 obtained from the thermoplastic resin or the thermoplastic resincomposition are sharpened with a thermal treatment.

The inventors made the following discovery, based on the results ofvarious studies on the causes of separation, which is a disadvantage ofthe conventional methods, between a sheet which constitutes, forexample, an inner liner layer, obtained from a thermoplastic resin or athermoplastic resin composition of a thermoplastic resin blended with anelastomer and a tie rubber sheet that undergoes vulcanizing adhesionwith the thermoplastic resin or the thermoplastic resin composition.

Specifically, when the abovementioned laminate sheet 1 is prepared withthe conventional method, large stress is produced in a rubber partsandwiched from above and below by the sheet 2 that is obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer and that has significantstiffness, in the vicinity of a lap splice part S at both ends of thelaminate sheet 1 as illustrated in FIGS. 2A and 2B, and as a result ofthe stress, it is thought that cracks are produced at a distal end partvicinity 4 of the sheet 2 obtained from the thermoplastic resin or thethermoplastic resin composition, and separation is produced as thecracks grow larger.

In contrast, the method for manufacturing a pneumatic tire of thepresent invention includes sharpening with a thermal treatment conductedon the distal end parts of the sheet 2 obtained from the thermoplasticresin or the thermoplastic resin composition, the sharpening beingconducted at a stage after cutting the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition into lengthsto be supplied to the step for lap splicing and before a tirevulcanization molding step.

The sharpening may be conducted in such a way that the sharpening isconducted solely on the sheet 2 obtained from the thermoplastic resin orthe thermoplastic resin composition and then the lamination with therubber 3 is conducted, or may be conducted after the lamination of thesheet 2 obtained from the thermoplastic resin or the thermoplastic resincomposition with the rubber 3. In this way, the sharpening may beconducted on the distal end parts of the single sheet 2 obtained fromthe thermoplastic resin or the thermoplastic resin composition or ondistal end parts of the sheet 2 obtained from the thermoplastic resin orthe thermoplastic resin composition in a state of being laminated intothe laminate sheet 1, generally before the laminate sheet 1 is woundonto the tire molding drum. However, the sharpening may be conducted byconducting the thermal treatment in a green tire state after thelaminate sheet 1 has been wound onto the tire molding drum. In thiscase, while the thermal treatment mainly on the distal end part of thesheet 2 obtained from the thermoplastic resin or the thermoplastic resincomposition that is exposed at the outer surface of the splice part (theeffect of the process does not extend to the embedded distal end parts),the effect of the sharpening due to the thermal treatment of the presentinvention is sufficiently demonstrated.

In either case, as illustrated in FIG. 1A, the method of the presentinvention involves the preparation of a green tire (not shown) havingthe sheet 2 obtained from the thermoplastic resin or the thermoplasticresin composition of a thermoplastic resin blended with an elastomer forwhich a sharpened portion 5 is formed in the vicinity of the distal endsthereof.

FIG. 1B is a model illustrating the state illustrated in FIG. 1A afterthe vulcanization molding.

Due to the formation of the sharpened portion 5 in the vicinity of thedistal ends of the sheet 2 obtained from the thermoplastic resin or thethermoplastic resin composition even after the tire vulcanizationmolding, the thicknesses of the above and below pair of sheets 2 thatare obtained from the thermoplastic resin or the thermoplastic resin ofa thermoplastic resin blended with an elastomer and that have a largestiffness, become thinner at the distal end part vicinity 4, andmoreover, stress due to widening of the surface area of the interfacebetween the sheet 2 and the rubber 3 is distributed and, as a result,stress produced in the rubber part sandwiched between the sheets 2 isreduced and distributed and thus mitigated. After the use of the tirehas started, an effect is achieved of preventing the occurrence of theseparation phenomenon between the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition and the tierubber sheet 3 that undergoes the vulcanizing adhesion.

In the present invention, when the “sharpening with a thermal treatmentconducted on the distal end parts of the sheet obtained from thethermoplastic resin or the thermoplastic resin composition” refersmerely to the use of a normal blade to cut the sheet obtained from thethermoplastic resin or the thermoplastic resin composition at a normaltemperature, while a cut section thereof has a vertical cross-sectionend surface in the planar direction of the sheet as seen in the sheetwidth direction (FIG. 2A), the sheet 2 according to the presentinvention has a sharpened portion 5 in which the cross-section endsurface of the sheet 2 is subject to the sharpening to gradually becomethinner toward the distal end and the thermal treatment is conducted onthe cross-section end parts of the sheet 2 in order to arrive at thisprofile shape as illustrated by the model in FIGS. 1A to 1C.

The thermal treatment may be performed with any non-contact or contactmethod. The non-contact method may include applying a burner or a flameto the sheet distal end surface, and the contact method may includeapplying the sheet distal end surface to a hot roll (heated roller) or ahot plate (heated plate) and the like.

The abovementioned shape “subject to the sharpening to gradually becomethinner toward the distal end” may signify a shape in which “roundness”is added in the vicinity of the distal end, and the abovementionedeffects of preventing the occurrence of cracks and the occurrence ofseparation are noticeable even when a shape with roundness is provided.The shape in which the distal end sharpening is conducted on the distalend of the sheet 2 is a shape in which the sharpened form issubstantially maintained before and after vulcanization, and thus theeffect of preventing the occurrence of cracks and the occurrence ofseparation is demonstrated after the use as a tire has started.

While the sharpening on the distal ends of the sheet 2 demonstrates theeffect even when having roundness as described above, in order to stablyachieve a high effect in particular, the sharpening is desirablyperformed so that a thickness T (mm) at a position located inward by adistance of (t×⅓) from the distal end of the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer, has a relationship thatsatisfies 0.1t≦T≦0.8t. FIG. 1C illustrates this relationship, and therelationship refers to a level of the thickness at the position locateda distance of (t/3) from the distal end, and desirably is 0.2t≦T≦0.6t.Here, t is the average thickness (mm) in the tire circumferentialdirection of a portion not subject to the sharpening of the sheet 2obtained from the thermoplastic resin or the thermoplastic resincomposition of a thermoplastic resin blended with an elastomer, and T isthe thickness (mm) of the sheet 2 at a position at a distance inward bya length of (t×⅓) from the distal end of the sheet 2 obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer.

A length L of the sharpened portion (5 in FIG. 1C) is L=(1.0 to20)×t(mm), that is, the distal end sharpened part is desirably conductedup to the position at a distance inward by the length L. Desirably, thelength is L=(1.0 to 10)×t(mm), or even more desirably, L=(1.0 to2.5)×t(mm).

While the shape of the sharpened portion desirably forms a cleanlytapered shape in the side cross-sectional shape as illustrated in FIGS.1A to 1C, since the effect may be achieved even without the cleanlytapered shape, the shape of the sharpened portion may be anasymmetrically tapered shape or a sharp tapered shape, and may have ashape that is curved in one direction (e.g., toward the tie rubberlayer), have a somewhat uneven shape, or have a shape provided with theabovementioned roundness.

In the present invention, while the sharpening on the distal ends of thesheet 2 is mainly conducted with the thermal treatment, the formationmay also be performed by using a heating and pressurization plate inconjunction.

When the thermal treatment is conducted on the distal end portions ofthe sheet 2 obtained from the thermoplastic resin composition of athermoplastic resin blended with an elastomer as in the presentinvention, a phenomenon occurs in which the elastomer present on theouter surface in the vicinity of the cut ends is covered with a coatingof the thermoplastic resin due to the flow of the thermoplastic resincaused by heating. Since the sheet 2 having this form demonstrates astronger vulcanizing adhesion state than when vulcanizing adhesionoccurs when the elastomer is exposed, this feature is also effective inpreventing the occurrence of cracks and/or the occurrence of separationin the method of the present invention. Generally, when the elastomer isexposed on the cut section of the laminate sheet, the elastomer hindersthe vulcanizing adhesion, and since the vulcanizing adhesion forcebetween the rubber and the sheet obtained from the thermoplastic resincomposition is reduced, it is desirable that the distal end is sharpenedso that the elastomer is not exposed.

In the present invention, the temperature of the thermal treatment isdesirably at or above the melting point of the thermoplastic resin orthe thermoplastic resin composition. This is because the process iseffective at or above the melting point of the thermoplastic resin orthe thermoplastic resin composition to enable the distal ends of thethermoplastic resin or the thermoplastic resin composition to be easilyand effectively sharpened.

When the thermal treatment is conducted solely on the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition, thethermal treatment may be conducted at a temperature at or above themelting point of the thermoplastic resin or the thermoplastic resincomposition and at or below (the melting point of the thermoplasticresin or the thermoplastic resin composition +250° C.). When conductedsolely on the sheet, the problems of hardening, degradation, ordeterioration and the like do not occur even with a thermal treatment ata relatively high temperature since the laminated rubber is not present.

Conversely, when conducting the thermal treatment on the laminate sheetin which the sheet obtained from the thermoplastic resin or thethermoplastic resin composition is laminated with the rubber, thethermal treatment is desirably conducted at a temperature at or abovethe melting point of the thermoplastic resin or the thermoplastic resincomposition and at or below (the melting point of the thermoplasticresin or the thermoplastic resin composition +180° C.). This is becausethe thermal treatment is desirably conducted at a relatively lowtemperature in order to not cause an adverse effect on the rubber due tothe thermal treatment when the thermal treatment is conducted on thelaminate sheet.

FIG. 3 is a partial fragmented perspective view illustrating one exampleof an aspect of the pneumatic tire according to the method formanufacturing a pneumatic tire of the present invention.

A pneumatic tire T is provided so that side wall portions 12 and beadportions 13 communicate on the left and right with a tread portion 11.On the tire inner side thereof, a carcass layer 14 that acts as aframework for the tire is provided so as to extend between the left andright bead portions 13 in the tire width direction. Two belt layers 15composed of steel cords are provided on the outer circumferential sideof the carcass layer 14 corresponding to the tread portion 11. The arrowX indicates the tire circumferential direction. An inner liner layer 10formed by lap splicing according to the method of the present inventionis disposed on the inside of the carcass layer 14, and a lap splice partS (both the S of FIG. 1 and FIG. 2) of the inner liner layer 10 ispresent and extends in the tire width direction.

In the pneumatic tire according to the present invention, the occurrenceof cracks that often occur conventionally in the vicinity of the lapsplice part S on the tire inner circumferential surface, and theoccurrence of cracks between the tie rubber layer 3 and the sheet 2obtained from the thermoplastic resin or the thermoplastic resincomposition that form the inner liner layer 10, and moreover theoccurrence of separation, are suppressed and durability is noticeablyimproved.

The effect according to the method for manufacturing a pneumatic tireaccording to the present invention is the same even when an item thathas the lap splice part S is used as a reinforcing sheet inside thepneumatic tire instead of being used as the inner liner layer.

While the overlapping length of the lap splice part S depends on thelocation of use and on the tire size, generally, the length is desirablyaround 7 to 20 mm, or more desirably around 8 to 15 mm. If theoverlapping length is too large, uniformity tends to become worse, andif the overlapping length is too small, there is a risk that the splicepart may open during molding.

The laminate sheet is not limited to one sheet and one or more than onesheet may be used. Both ends of the laminate sheet may be lap-splicedwhen one sheet is used, and mutual end parts may be lap-spliced to formone ring when a plurality of sheets is used. If the overlapping lengthof the lap splice part S and the number of laminate sheets to be usedare both set appropriately, the manufacturing method of the presentinvention may be applied to a method for manufacturing a pneumatic tireof all dimensions, and the prescribed effect of the present inventionmay be achieved.

The thermoplastic resin to be used in the present invention ispreferably a polyamide resin, [e.g., nylon 6 (N6), nylon 66 (N66), nylon46 (N46), nylon 11 (N11), nylon 12 (N12), nylon 610 (N610), nylon 612(N612), nylon 6/66 copolymer (N6/66), nylon 6/66/610 copolymer(N6/66/610), nylon MXD6 (MXD6), nylon 6T, nylon 9T, nylon 6/6Tcopolymer, nylon 66/PP copolymer, nylon 66/PPS copolymer] and anN-alkoxyalkyl compound thereof, e.g., a methoxymethyl compound of nylon6, a methoxymethyl compound of a nylon 6/610 copolymer, or amethoxymethyl compound of nylon 612; a polyester resin [e.g., anaromatic polyester such as polybutylene terephthalate (PBT),polyethylene terephthalate (PET), polyethylene isophthalate (PEI), aPET/PEI copolymer, polyarylate (PAR), polybutylene naphthalate (PBN), acrystal polyester, a polyoxyalkylene diimide acid/polybutyleneterephthalate copolymer]; a polynitrile resin [e.g., polyacrylonitrile(PAN), polymethacrylonitrile, an acrylonitrile/styrene copolymer (AS), a(meta)acrylonitrile/styrene copolymer, a(meta)acrylonitrile/styrene/butadiene copolymer], a polymethacrylateresin [e.g., polymethyl-methacrylate (PMMA), polyethyl-methacrylicacid], a polyvinyl resin [e.g., vinyl acetate, a polyvinyl alcohol(PVA), a vinyl alcohol/ethylene copolymer (EVOH), polyvinylidenechloride (PDVC), polyvinylchloride (PVC), a vinyl chloride/vinylidenechloride copolymer, a vinylidene chloride/methylacrylate copolymer, avinylidene chloride/acrylonitrile copolymer (ETFE)], a cellulose resin[e.g., cellulose acetate, cellulose acetate butyrate], a fluoride resin[e.g., polyvinylidene difluoride (PVDF), polyvinyl fluoride (PVF),polychlorofluoroethylene (PCTFE), a tetrafluoroethylene/ethylenecopolymer], or an imide resin [e.g., an aromatic polyimide (PI)].

In particular, the thermoplastic resin desirably includes at least onetype of polyamide resin, polyester resin, polynitrile resin,polymethacrylate resin, polyvinyl resin, cellulose resin, fluorideresin, or imide resin.

The elastomer and the thermoplastic resin constitute the thermoplasticresin composition used in the present invention, and the abovementioneditems may be used as the thermoplastic resin. The elastomer to be useddesirably includes a diene-based rubber and a hydrogenate thereof [e.g.,natural rubber (NR), isoprene rubber (IR), epoxidized natural rubber,styrene butadiene rubber (SBR), butadiene rubber (BR, high cis-BR, lowcis-BR), nitrile rubber (NBR), hydrogenated NBR, hydrogenated SBR], anolefin rubber [e.g., ethylene propylene rubber (EPDM, EPM), maleic acidethylene propylene rubber (M-EPM), butyl rubber (IIR), an isobutyleneand aromatic vinyl or diene-based monomer copolymer, acrylic rubber(ACM), an ionomer], a halogen-containing rubber [e.g., Br-IIR, CI-IIR, abrominated isobutylene-p-methylstyrene copolymer (BIMS), chloroprenerubber (CM), a hydrin rubber (CHR), chlorosulfonated polyethylene rubber(CSM), chlorinated polyethylene rubber (CM), chlorinated polyethylenerubber modified with maleic acid (M-CM)], a silicon rubber [e.g., methylvinyl silicon rubber, dimethyl silicon rubber, methylphenyl vinylsilicon rubber], a sulfur-containing rubber [e.g., polysulfide rubber],a fluororubber [e.g., a vinylidene fluoride rubber, a vinyl ether rubbercontaining fluoride, a tetrafluoroethylene-propylene rubber, asilicon-based rubber containing fluoride, a phosphazene rubbercontaining fluoride], and a thermoplastic elastomer [e.g., a styreneelastomer, an olefin elastomer, an ester elastomer, a urethaneelastomer, a polyamide elastomer]. The elastomer includes at least onetype of diene rubber, diene rubber hydrogenate, halogen-containingrubber, silicon rubber, sulfur-containing rubber, fluororubber, orthermoplastic elastomer.

Moreover, when the compatibility is different upon blending by combiningthe previously specified thermoplastic resin and the previouslyspecified elastomer, a suitable compatibility agent may be used as athird component to enable compatibilization of both the resin and theelastomer. By mixing the compatibility agent in the blend, interfacialtension between the thermoplastic resin and the elastomer is reduced,and as a result, the particle diameter of the elastomer that forms thedispersion layer becomes very small and thus the characteristics of bothcomponents may be realized effectively. This type of compatibility agentmay generally have a structure of a copolymer having a structure of oneor both of the thermoplastic resin and the elastomer, or a copolymerhaving an epoxy group, a carbonyl group, a halogen group, an aminogroup, an oxazoline group, and/or a hydroxy group or the like that isable to react with the thermoplastic resin or the elastomer. While thetype of compatibility agent may be selected according to the type ofthermoplastic resin and elastomer to be blended, such a compatibilityagent generally includes: a styrene/ethylene butylene block copolymer(SEBS) or a maleic acid modified compound thereof; an EPDM, EPM,EPDM/styrene or EPDM/acrylonitrile graft copolymer or a maleic acidmodified compound thereof; a styrene/maleic acid copolymer, or areactive phenoxy, and the like. The blending quantity of such acompatibility agent, while not being limited, is preferably 0.5 to 10parts by weight with respect to 100 parts by weight of the polymercomponent (total of the thermoplastic resin and the elastomer).

A composition ratio of the specific thermoplastic resin and theelastomer in the thermoplastic resin composition of a thermoplasticresin blended with an elastomer, while not limited in particular, may bedetermined as appropriate to establish a dispersed structure as adiscontinuous phase of the elastomer in the matrix of the thermoplasticresin, and is desirably a range of a weight ratio of 90/10 to 30/70.

A compatibility agent of another polymer within a range that does notharm the characteristics required for an inner liner or a reinforcingmember may be blended with the thermoplastic resin composition of athermoplastic resin blended with an elastomer in the present invention.The purposes of mixing such a polymer are to improve the compatibilitybetween the thermoplastic resin and the elastomer, to improve themolding processability of the material, to improve the heat resistance,to reduce cost, and so on. Examples of the material used for the polymerinclude polyethylene (PE), polypropylene (PP), polystyrene (PS), ABS,SBS, and polycarbonate (PC). Furthermore, a reinforcing agent such as afiller (calcium carbonate, titanium oxide, alumina), carbon black, orwhite carbon, a softening agent, a plasticizer, a processing aid, apigment, a dye, or an anti-aging agent generally compounded with polymercompounds may be optionally compounded so long as the characteristicsrequired for an inner liner are not harmed. The thermoplastic resincomposition has a structure in which the elastomer is distributed as adiscontinuous phase in the matrix of the thermoplastic resin. Byadopting such a structure, it becomes possible to provide the innerliner or the reinforcing member with sufficient flexibility andsufficient stiffness that is attributed to the effect of the resin layeras continuous phase. Furthermore, it becomes possible to obtain, duringmolding, a molding processability equivalent to the thermoplastic resinregardless of the amount of the elastomer.

The Young's moduli of the thermoplastic resin and the elastomer that maybe used in the present invention, while not limited in particular, areboth preferably 1 to 500 MPa, and more preferably 50 to 500 MPa.

EXAMPLES Working Examples 1 and 10, Comparative Example 1

A detailed explanation of the method for manufacturing a pneumatic tireof the present invention is provided based on the following workingexamples.

As illustrated in Table 1, a thermoplastic resin composition having a50/50 blend of N6/66 as the thermoplastic resin and BIMS as theelastomer, and having a thickness (t) of 0.13 mm and a melting point of190° C. was prepared as the thermoplastic resin composition sheet.

Tie rubber with a thickness of 0.7 mm and having the compositionillustrated in Table 2 was prepared as the tie rubber layer.

TABLE 1 Parts by mass BIMS^(a)) “Exxpro 3035” Made by Exxon 100 MobileChemical Co. Zinc oxide “Zinc oxide type III” made by 0.5 Seido ChemicalIndustry Co., Ltd. Stearic acid Industrial stearic acid 0.2 Zincstearate “Zinc stearate” made by NOF 1 Corporation N6/66 “UBE Nylon5033B” made by Ube 100 Industries, Ltd. Modified EEA^(b)) “HPR-AR 201”made by Du Pont 10 Mitsui Polychemicals Co., Ltd. Reference:^(a))Brominated isobutylene-p-methylstyrene copolymer ^(b))Maleicanhydride modified ethylene - ethylacrylate copolymer

TABLE 2 Parts by mass Styrene butadiene rubber Made by Zeon Corporation50 “Nipol 1502” Natural rubber SIR-20 50 Carbon black Made by TokaiCarbon Co., Ltd 60 “Seast V” Stearic acid Industrial stearic acid 1Aromatic oil Made by Showa Shell Sekiyu KK 7 Desolex No. 3″ Zinc oxide“Zinc oxide type III” made by 3 Seido Chemical Industry Co., Ltd.Modified resorcin Made by Taoka Chemical Co., Ltd. 2 formaldehydecondensate “Sumikanol 620” Methylene donor Modified ethermethylolmelamine 6 Made by Taoka Chemical Co., Ltd. “Sumikanol 507 AP”Sulfur 5% oil-extension treated sulfur 6 Vulcanization acceleratorDi-2-benzothiazolyl disulfide 2.2 Made by Ouchi Shinko ChemicalIndustrial Co., Ltd. “NOCCELER DM”

Tests were performed for two cases including a case in which thethermoplastic resin composition sheet was prepared by performing thethermal treatment solely on the sheet after cutting (working examples 1,2, 3, 4, 6, 8, 10 and comparative example 1), and a case in which thethermoplastic resin composition sheet was laminated with the above tierubber layer and then cut, and the thermal treatment was performed onthe laminated body (working examples 5, 7, 9). The procedures in eachcase were performed as described below as in (1) and (2).

(1) When the thermal treatment was conducted solely on the sheet:

-   -   (a) the above thermoplastic resin composition sheet was made        (t=0.13 mm);    -   (b) the thermoplastic resin composition sheet was cut into        certain lengths;    -   (c) the distal ends of the thermoplastic resin composition sheet        were subject to the thermal treatment under the conditions        described in Table 3;    -   (d) the rubber layer that undergoes vulcanizing adhesion with        the thermoplastic resin composition sheet was manufactured;    -   (e) the laminated body was manufactured by pre-assembly of the        thermoplastic resin composition sheet and the rubber layer;    -   (f) the laminated body was lap-spliced on the molding drum and        then vulcanized to manufacture a tire;    -   (g) the manufactured tire was evaluated after a certain road        test.

(2) When the laminated body of the sheet and the rubber were subject tothe thermal treatment:

-   -   (a) the above thermoplastic resin composition sheet was made        (t=0.13 mm);    -   (b) the rubber layer that undergoes vulcanizing adhesion with        the thermoplastic resin composition sheet was manufactured;    -   (c) the laminated body was manufactured by pre-assembly of the        thermoplastic resin composition sheet and the rubber layer;    -   (d) the obtained laminated body was cut into certain sizes;    -   (e) the distal ends of the laminated body were subject to the        thermal treatment under the conditions described in Table 3;    -   (f) the laminated body was lap-spliced on the molding drum and        then vulcanized to manufacture a tire;    -   (g) the manufactured tire was evaluated after a certain road        test.

The size of the test tires was 215/70R15 98H and two samples werefabricated for each working example and comparative example.

The samples were attached to a 15×6.5JJ standard rim conforming to JapanAutomobile Tyre Manufacturers Association (JATMA) standards, and thetire pressure was set to the maximum air pressure (240 KPa) according tothe JATMA standard.

The evaluation of the tires was conducted by taking samples of thelaminate sheet according to the present invention in the inner linerlayers in the cavity of the test tires and then comparing the occurrenceof cracks and separation in the vicinity of the splice portions andcomparing the conditions in other portions of the tire. The pneumatictires were driven at 7.35 kN for 50,000 km, and then the presence of theoccurrence of cracks and the occurrence of separation in the vicinity ofthe lap splice portions of the inner liner layers in the cavities of thetest tires was examined in comparison to the conditions in otherportions of the tire.

Results are shown in Table 3. The effects (effect of suppression ofcracks and separation) were evaluated in four categories of “excellent,”“good,” “permissible,” and “not permissible.”

No problems occurred in particular in the vicinity of the spliceportions or in other places after being driven for 50,000 km in theembodiments of the present invention.

The melting points of the thermoplastic resin and the thermoplasticresin composition in the above explanation are values derived accordingto differential scanning calorimetry (DSC).

TABLE 3 Distal Use of Time of Distal end end thermal thermal Treatmentshape T shape treatment treatment temperature (mm) T/t ResultComparative No Single sheet No 0.13 1.0 Not Example 1 permissibleWorking Present Single sheet Melting 0.08 0.62 Excellent Example 1point + 60° C. Working Present Single sheet Melting 0.09 0.69Permissible Example 2 point + 30° C. Working Present Single sheetMelting 0.10 0.77 Permissible Example 3 point Working Present Singlesheet Melting 0.06 0.46 Excellent Example 4 point + 90° C. WorkingPresent Laminate of Melting 0.06 0.46 Excellent Example 5 sheet/rubberpoint + 90° C. Working Present Single sheet Melting 0.04 0.31 ExcellentExample 6 point + 120° C. Working Present Laminate of Melting 0.04 0.31Good Example 7 sheet/rubber point + 120° C. Working Present Single sheetMelting 0.03 0.23 Excellent Example 8 point + 150° C. Working PresentLaminate of Melting 0.03 0.23 Permissible Example 9 sheet/rubber point +150° C. Working Present single sheet Melting 0.02 0.15 Good Example 10point + 200° C.

Reference Numerals

-   1: Laminate sheet-   2: Sheet of thermoplastic resin or thermoplastic resin composition    of thermoplastic resin blended with an elastomer-   3: Tie rubber layer-   4: Vicinity of distal end part of the sheet 2 of thermoplastic resin    or thermoplastic resin composition-   5: Sharpened portion-   10: Inner liner layer-   11: Tread portion-   12: Side wall portion-   13: Bead-   14: Carcass layer-   15: Belt layer-   L: Length of portion subject to distal end sharpening-   S: Lap splice part-   X: Tire circumferential direction

1. A method for manufacturing a pneumatic tire, comprising: lap splicingend parts of a laminate sheet comprising a sheet obtained from athermoplastic resin or a thermoplastic resin composition of athermoplastic resin blended with an elastomer laminated with a rubberthat undergoes vulcanizing adhesion with the thermoplastic resin or thethermoplastic resin composition; and sharpening distal end parts of thesheet obtained from the thermoplastic resin or the thermoplastic resincomposition with a thermal treatment after the sheet obtained from thethermoplastic resin or the thermoplastic resin composition is cut intolengths to be supplied to the lap-splicing step, and at a stage beforetire vulcanization molding.
 2. The method for manufacturing a pneumatictire according to claim 1, wherein a temperature of the thermaltreatment is at or above the melting point of the thermoplastic resin orthe thermoplastic resin composition.
 3. The method for manufacturing apneumatic tire according to claim 2, wherein, when the thermal treatmentis conducted solely on the sheet obtained from the thermoplastic resinor the thermoplastic resin composition, the thermal treatment isconducted at a temperature at or above the melting point of thethermoplastic resin or the thermoplastic resin composition and at orbelow (the melting point of the thermoplastic resin or the thermoplasticresin composition +250° C.).
 4. The method for manufacturing a pneumatictire according to claim 2, wherein, when the thermal treatment isconducted on the laminate sheet in which the sheet obtained from thethermoplastic resin or the thermoplastic resin composition is laminatedwith the rubber that undergoes vulcanizing adhesion with thethermoplastic resin or the thermoplastic resin composition, the thermaltreatment is conducted at a temperature at or above the melting point ofthe thermoplastic resin or the thermoplastic resin composition and at orbelow (the melting point of the thermoplastic resin composition +180°C.).
 5. The method for manufacturing a pneumatic tire according to claim1, wherein, the sharpening has a relationship in which a thickness T(mm) at a position at a distance inward by a length of (t×⅓) from thedistal end of the sheet obtained from the thermoplastic resin or thethermoplastic resin composition satisfies the equation 0.1t≦T≦0.8t,where, t: average thickness (mm) in the tire circumferential directionof a portion not subject to the sharpening of the sheet obtained fromthe thermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer, T: thickness (mm) at aposition at a distance inward by a length of (t×⅓) from the distal endof the sheet obtained from the thermoplastic resin or the thermoplasticresin composition of a thermoplastic resin blended with an elastomer. 6.The method for manufacturing the pneumatic tire according to claim 1,wherein, the thermoplastic resin includes at least one type of apolyamide resin, a polyester resin, a polynitrile resin, apolymethacrylate resin, a polyvinyl resin, a cellulose resin, a fluorideresin, or an imide resin.
 7. The method for manufacturing the pneumatictire according to claim 1, wherein, the elastomer includes at least onetype of a diene-based rubber, a diene-based rubber hydrogenate, ahalogen-containing rubber, a silicon rubber, a sulfur-containing rubber,a fluororubber, or a thermoplastic elastomer.
 8. The method formanufacturing the pneumatic tire according to claim 1, wherein, one or aplurality of the laminate sheets are used, and both end parts arelap-spliced when one sheet is used, and mutual end parts are lap-splicedwhen a plurality of sheets are used.
 9. The method for manufacturing apneumatic tire according to claim 2, wherein, the sharpening has arelationship in which a thickness T (mm) at a position at a distanceinward by a length of (t×⅓) from the distal end of the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin compositionsatisfies the equation 0.1t≦T≦0.8t, where, t: average thickness (mm) inthe tire circumferential direction of a portion not subject to thesharpening of the sheet obtained from the thermoplastic resin or thethermoplastic resin composition of a thermoplastic resin blended with anelastomer, T: thickness (mm) at a position at a distance inward by alength of (t×⅓) from the distal end of the sheet obtained from thethermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer.
 10. The method formanufacturing a pneumatic tire according to claim 3, wherein, thesharpening has a relationship in which a thickness T (mm) at a positionat a distance inward by a length of (t×⅓) from the distal end of thesheet obtained from the thermoplastic resin or the thermoplastic resincomposition satisfies the equation 0.1t≦T≦0.8t, where, t: averagethickness (mm) in the tire circumferential direction of a portion notsubject to the sharpening of the sheet obtained from the thermoplasticresin or the thermoplastic resin composition of a thermoplastic resinblended with an elastomer, T: thickness (mm) at a position at a distanceinward by a length of (t×⅓) from the distal end of the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer.
 11. The method formanufacturing a pneumatic tire according to claim 4, wherein, thesharpening has a relationship in which a thickness T (mm) at a positionat a distance inward by a length of (t×⅓) from the distal end of thesheet obtained from the thermoplastic resin or the thermoplastic resincomposition satisfies the equation 0.1t≦T≦0.8t, where, t: averagethickness (mm) in the tire circumferential direction of a portion notsubject to the sharpening of the sheet obtained from the thermoplasticresin or the thermoplastic resin composition of a thermoplastic resinblended with an elastomer, T: thickness (mm) at a position at a distanceinward by a length of (t×⅓) from the distal end of the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer.
 12. The method formanufacturing the pneumatic tire according to claim 2, wherein, thethermoplastic resin includes at least one type of a polyamide resin, apolyester resin, a polynitrile resin, a polymethacrylate resin, apolyvinyl resin, a cellulose resin, a fluoride resin, or an imide resin.13. The method for manufacturing the pneumatic tire according to claim3, wherein, the thermoplastic resin includes at least one type of apolyamide resin, a polyester resin, a polynitrile resin, apolymethacrylate resin, a polyvinyl resin, a cellulose resin, a fluorideresin, or an imide resin.
 14. The method for manufacturing the pneumatictire according to claim 4, wherein, the thermoplastic resin includes atleast one type of a polyamide resin, a polyester resin, a polynitrileresin, a polymethacrylate resin, a polyvinyl resin, a cellulose resin, afluoride resin, or an imide resin.
 15. The method for manufacturing thepneumatic tire according to claim 5, wherein, the thermoplastic resinincludes at least one type of a polyamide resin, a polyester resin, apolynitrile resin, a polymethacrylate resin, a polyvinyl resin, acellulose resin, a fluoride resin, or an imide resin.
 16. The method formanufacturing the pneumatic tire according to claim 2, wherein, theelastomer includes at least one type of a diene-based rubber, adiene-based rubber hydrogenate, a halogen-containing rubber, a siliconrubber, a sulfur-containing rubber, a fluororubber, or a thermoplasticelastomer.
 17. The method for manufacturing the pneumatic tire accordingto claim 3, wherein, the elastomer includes at least one type of adiene-based rubber, a diene-based rubber hydrogenate, ahalogen-containing rubber, a silicon rubber, a sulfur-containing rubber,a fluororubber, or a thermoplastic elastomer.
 18. The method formanufacturing the pneumatic tire according to claim 4, wherein, theelastomer includes at least one type of a diene-based rubber, adiene-based rubber hydrogenate, a halogen-containing rubber, a siliconrubber, a sulfur-containing rubber, a fluororubber, or a thermoplasticelastomer.
 19. The method for manufacturing the pneumatic tire accordingto claim 5, wherein, the elastomer includes at least one type of adiene-based rubber, a diene-based rubber hydrogenate, ahalogen-containing rubber, a silicon rubber, a sulfur-containing rubber,a fluororubber, or a thermoplastic elastomer.
 20. The method formanufacturing the pneumatic tire according to claim 1, wherein: atemperature of the thermal treatment is at or above the melting point ofthe thermoplastic resin or the thermoplastic resin composition; when thethermal treatment is conducted solely on the sheet obtained from thethermoplastic resin or the thermoplastic resin composition, the thermaltreatment is conducted at a temperature at or above the melting point ofthe thermoplastic resin or the thermoplastic resin composition and at orbelow (the melting point of the thermoplastic resin or the thermoplasticresin composition +250° C.); when the thermal treatment is conducted onthe laminate sheet in which the sheet obtained from the thermoplasticresin or the thermoplastic resin composition is laminated with therubber that undergoes vulcanizing adhesion with the thermoplastic resinor the thermoplastic resin composition, the thermal treatment isconducted at a temperature at or above the melting point of thethermoplastic resin or the thermoplastic resin composition and at orbelow (the melting point of the thermoplastic resin composition +180°C.); the sharpening has a relationship in which a thickness T (mm) at aposition at a distance inward by a length of (t×⅓) from the distal endof the sheet obtained from the thermoplastic resin or the thermoplasticresin composition, satisfies the equation 0.1t≦T≦0.8t, where, t: averagethickness (mm) in the tire circumferential direction of a portion notsubject to the sharpening of the sheet obtained from the thermoplasticresin or the thermoplastic resin composition of a thermoplastic resinblended with an elastomer, T: thickness (mm) at a position at a distanceinward by a length of (t×⅓) from the distal end of the sheet obtainedfrom the thermoplastic resin or the thermoplastic resin composition of athermoplastic resin blended with an elastomer; the thermoplastic resinincludes at least one type of a polyamide resin, a polyester resin, apolynitrile resin, a polymethacrylate resin, a polyvinyl resin, acellulose resin, a fluoride resin, or an imide resin; the elastomerincludes at least one type of a diene-based rubber, a diene-based rubberhydrogenate, a halogen-containing rubber, a silicon rubber, asulfur-containing rubber, a fluororubber, or a thermoplastic elastomer;and one or a plurality of laminate sheets are used, and both end partsare lap-spliced when one sheet is used, and mutual end parts arelap-spliced when a plurality of sheets are used.